Hydrogen Embrittlement of 4340 Steel as a Result of Corrosion of Porous Electroplated Cadmium
CORROSION (1972) 28 (6): 231–232.
Article history
Received:
February 01 1972
Citation
JOHN G. RINKER, ROBERT F. HOCHMAN; Hydrogen Embrittlement of 4340 Steel as a Result of Corrosion of Porous Electroplated Cadmium. CORROSION 1 June 1972; 28 (6): 231–232. doi: https://doi.org/10.5006/0010-9312-28.6.231
Download citation file:
Sign in
Don't already have an account? Register
Client Account
You could not be signed in. Please check your email address / username and password and try again.
Could not validate captcha. Please try again.
Sign in via your Institution
Sign in via your InstitutionCiting articles via
Improving the Long—Term Protection of Buried Steel Tanks: Considering the Impact of Temperature and Extended Sacrificial Anodes
Mohammad Javad Shirshahi, Seyed Farshid Chini, Peyman Taheri, Abraham Mansouri
Corrosion prediction model for long-distance pipelines based on NLFE-NGO-ELM
Xingyu Du, Yujie Dai, Bailing Zheng, Xinqi Zhu
Identification of Synergistic Interactions in Green Corrosion Inhibitor Mixtures by Molecular Modeling
Carlos M. Menendez, Oleg A. Mazyar, Sunder Ramachandran, Tracey Jackson
Resistance of the welded joint of X70 steel for main gas pipelines against corrosion-mechanical cracking under cathodic polarization in near-neutral pH solutions
Lyudmila Nyrkova, Larysa Goncharenko, Yuriy Lisovskiy, Leonid Faynberg, Valeriy Kostin
Effect of Non-Essential Alloying Elements and Solution pH on Corrosion Behavior of Al-Mg Alloys Fabricated by Cold Spray Deposition
Munsu Kim, Luke N. Brewer, Gregory W. Kubacki