Clinical Relevance One-step self-etch adhesive systems provide a clinical time gain, decreasing the number of clinical steps. When a clinician is able to follow a simpler process of adhesion there is less chance of adhesive failure. SUMMARY Objective: A systematic review and meta-analyses were performed to evaluate whether one-step self-etching (1SSE) adhesive systems are as effective as two-step self-etching (2SSE) adhesives in noncarious cervical lesion (NCCL) restorations. Methods: This systematic review was conducted according to the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-analyses (PRISMA) and recorded in the PROSPERO (CRD42018096747). Electronic systematic searches were conducted in the following databases: PubMed/MEDLINE, Scopus, and Cochrane Library for published articles. Only randomized clinical trials that compared 1SSE with 2SSE adhesives systems were selected. The outcomes were retention, postoperative sensitivity, secondary caries, color match, marginal discoloration, marginal adaptation, and anatomical form. Results: The searches resulted in 476 studies. After applying the eligibility criteria, five randomized controlled trials were selected in which 822 restorations in NCCLs were distributed in 237 patients. The results showed no statistical difference between 1SSE and 2SSE in relation to retention ( p =0.23; relative risk [RR]=1.55; 95% confidence interval [CI]=0.76, 3.19), postoperative sensitivity ( p =0.50; RR=3.00; 95% CI=0.13, 70.64), Secondary caries ( p =0.63; RR=0.68; 95% CI=0.14, 3.31), color match ( p =0.41; RR=0.64; 95% CI=0.23, 1.83), marginal discoloration ( p =0.93; RR=1.02; 95% CI=0.65, 1.61), and anatomical form ( p =0.56; RR=1.38; 95% CI=0.46, 4.13). However there was statistical difference in relation to marginal adaptation ( p =0.01; RR=1.95; 95% CI=1.14, 3.34). Conclusion: This systematic review with meta-analysis revealed that both 1SSE and 2SSE adhesive systems have comparable clinical effectiveness in a follow-up period of 12 to 24 months, except in relation to marginal adaptation.

SUMMARY Purpose: The purpose of this in vitro study was to evaluate the resistance and patterns of fracture of endodontically treated maxillary premolars (ETPs) restored with different methods. Methods and Materials: Mesio-occluso-distal cavities were prepared in 50 extracted caries-free human maxillary premolars after endodontic treatment. The teeth were divided into five groups (n=10), according to the restorative method. G1: intact teeth (control group); G2: conventional composite resin; G3: conventional composite resin with a horizontal glass fiber post inserted between buccal and palatal walls; G4: bulk-fill flowable and bulk-fill restorative composites; and G5: ceramic inlay. For direct restorations, Filtek Z350 XT, Filtek Bulk Fill Flowable Restorative, and Filtek Bulk Fill Posterior Restorative were used. Indirect restorations were fabricated from a pressable lithium disilicate glass-ceramic (IPS e-max Press) and adhesively cemented (RelyX Ultimate). All specimens were subjected to thermocycling (5°C to 55°C/5000 cycles) and additionally submitted to cyclic loading 50,000 times in an Electro-Mechanical Fatigue Machine. Next, the specimens were subjected to a compressive load at a crosshead speed of 1 mm/min until fracture. The fractured specimens were analyzed to determine the fracture pattern using a stereomicroscope, and then representative specimens were carbon coated to allow for the studying of the fracture surface under scanning electron microscopy. One-way analysis of variance (ANOVA) was used to compare fracture resistance of the groups. The results of fracture patterns were submitted to the Fisher exact test (α=0.05). Results: All specimens survived fatigue. Mean (standard deviation) failure loads (N) for groups were as follows: G1: 949.6 (331.5); G2: 999.6 (352.5); G3: 934.5 (233.6); G4: 771.0 (147.4); and G5: 856.7 (237.5). The lowest fracture resistance was recorded for G4, and the highest ones were recorded for G2, followed by that of G1 and G3. One-way ANOVA did not reveal significant differences between groups ( p >0.05). The highest repairable fracture rates were observed in G1 (100%) and G3 (80%). Conclusions: ETPs restored with conventional composite resin with or without horizontal fiber post, bulk-fill composite, and ceramic inlay showed fracture resistance similar to that of sound teeth. Conventional composite resin restorations exhibited the highest prevalence of unrepairable fractures, and the insertion of a horizontal fiber post decreased this prevalence. Intact teeth showed 100% of repairable fractures. It is difficult to extrapolate the results directly to a clinical situation due to the limitations of this study.

SUMMARY This article presents a case report for the treatment of a patient with a flared root. The patient was treated with a bulk-fill flowable composite. This innovative approach seems to be efficient in reinforcing flared roots. The advantages and disadvantages of the technique are presented.

SUMMARY This study aimed to evaluate the bond durability of dentin restorations bonded with light- or dual-cured etch-and-rinse adhesive systems. A three-step adhesive system (Scotchbond Multipurpose Plus), an acetone-based two-step adhesive system (Prime & Bond 2.1), and an ethanol-based two-step adhesive system (Excite) were tested. Both the light- and the dual-cured versions were evaluated. High C-factor dentin cavities were prepared on 120 bovine incisors, which were then restored with resin composite (n=10). The samples were stored in water for 24 hours, and half of them were subjected to additional degradation with 10% NaOCl for five hours. The push-out bond strength test was performed in a universal testing machine until failure. Failure modes were evaluated by scanning electron microscopy. Data were analyzed by three-way analysis of variance and Tukey tests ( p <0.05). The dual-cured adhesive system presented a higher immediate bond strength and durability than those that were light cured. The three-step adhesive system produced the highest values, whereas the acetone-based adhesive system produced the lowest result. Therefore, the use of dual-cured etch-and-rinse adhesive systems can induce increased bond durability to direct coronal dentin restorations.

SUMMARY This study was designed to evaluate in vitro the efficacy of a novel at-home bleaching technique using 10% or 16% carbamide peroxide modified by casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and its influence on the microhardness of bleached enamel. A total of 40 bovine incisors were divided into four groups (n=10) according to the bleaching agent used: 10% carbamide peroxide only; a blend of 10% carbamide peroxide and a CPP-ACP paste; 16% carbamide peroxide only; and a blend of 16% carbamide peroxide and a CPP-ACP paste. During the 14-day bleaching regimen, the samples were stored in artificial saliva. The Vickers microhardness and color of the teeth were assessed at baseline (T0) and immediately after the bleaching regimen (T14) using a microhardness tester and a spectrophotometer, respectively. The degree of color change was determined by the Commission Internationale de l'Eclariage (CIE) L*a*b* system (ΔE, ΔL*, Δa*, and Δb*) and Vita shade guide parameters. The data were analyzed by analysis of variance and the Tukey test ( p <0.05). The teeth that were bleached with a blend of peroxide (10% or 16%) and the CPP-ACP paste presented increased microhardness values at T14 compared with T0, whereas the samples that were bleached with peroxide only did not show any differences in their microhardness values. All of the bleaching agents were effective at whitening the teeth and did not show a statistically significant difference using the CIEL*a*b* system (ΔE, ΔL*, Δa*, and Δb*) or the Vita shade guide parameters. The use of a CPP-ACP paste with carbamide peroxide bleaching agents increased the bleached enamel's microhardness and did not have an influence on whitening efficacy.

Clinical Relevance According to finite element analysis, the zirconia ceramic post created higher stress levels in the post and slightly less in dentin compared with glass fiber posts. Resin cement with a high elastic modulus created higher stress levels in the cement layer. The different film thicknesses of cement did not create significant changes in stress levels. SUMMARY The current study evaluated the influence of two endodontic post systems and the elastic modulus and film thickness of resin cement on stress distribution in a maxillary central incisor (MCI) restored with direct resin composite using finite element analysis (FEA). A three-dimensional model of an MCI with a coronary fracture and supporting structures was performed. A static chewing pressure of 2.16 N/mm 2 was applied to two areas on the palatal surface of the composite restoration. Zirconia ceramic (ZC) and glass fiber (GF) posts were considered. The stress distribution was analyzed in the post, dentin and cement layer when ZC and GF posts were fixed to the root canals using resin cements of different elastic moduli (7.0 and 18.6 GPa) and different layer thicknesses (70 and 200 μm). The different post materials presented a significant influence on stress distribution with lesser stress concentration when using the GF post. The higher elastic modulus cement created higher stress levels within itself. The cement thicknesses did not present significant changes.